Perfluoroelastomers

ABSTRACT

Perfluoroelastomers curable by peroxidic way having glass transition temperature lower than −10° C. and an amount of —COF end groups in the polymer lower than the sensitivity limit of the method using the IR spectroscopy in Fourier transform described in the present application.

The present invention relates to perfluoroelastomers having a Tg (glass transition temperature) lower than −10° C. and an improved combination of mechanical and compression set properties in a wide range of temperatures, at high and at low temperatures.

More specifically the present invention relates to perfluoroelastomers having a Tg lower than −10° C. and substantially —COF end group free, said end groups being undetectable by the method indicated hereinafter. The perfluoroelastomers of the present invention show an improved molecular weight as shown by the improved intrinsic viscosity and are obtainable by a polymerization process with an improved productivity.

It is well known that perfluoroelastomers are polymers particularly useful in the aerospace, oil, petrochemical and semiconductor industry due to their combination of thermal and chemical resistance and of maintenance of good mechanical and compression set properties. However it is necessary that these polymers have an improved combination of the above properties in a wide temperature range, at high and at low temperatures.

Various perfluoroelastomers have been suggested in the prior art to obtain the combination of the above properties, highly requested by perfluoroelastomer users. However in the prior art the —COF end group values in perfluoroelastomers are not reported. The Applicant, after deep researches has found that, if the polymerization brings to polymers having —COF end groups, the perfluoroelastomers do not show high mechanical and elastic properties.

Various perfluoroelastomers wherein the glass transition temperature values are reported are known in the prior art. However in the prior art the combination of a low Tg and of improved mechanical and elastomeric properties at high and at low temperatures is not obtained.

U.S. Pat. No. 3,132,123 describes the preparation of perfluoroalkylvinylethers, their homopolymers and copolymers with TFE. The homopolymers are obtained under extreme experimental conditions, by using polymerization pressures from 4,000 to 18,000 atm. The general formula of the described vinylethers is the following: CF₂═CFOR⁰ _(F) wherein R⁰ _(F) is a perfluoroalkyl radical preferably from 1 to 5 carbon atoms. Tests carried out by the Applicant have shown that the homopolymer Tg is not very low and is of the order of −6° C.

U.S. Pat. No. 3,450,684 relates to vinylethers of formula: CF₂═CFO(CF₂CFX⁰O)_(n′)CF₂CF₂X⁰ wherein X⁰=F, Cl, CF₃, H and n′ can range from 1 to 20. Also the homopolymers obtained by UV polymerization are reported. The exemplified copolymers are not characterized with their mechanical and elastomeric properties at low temperatures.

U.S. Pat. No. 3,635,926 relates to the emulsion copolymerization of perfluorovinylethers with TFE. It is stressed that the presence of —COF end groups makes polymers unstable. The same was already reported in U.S. Pat. No. 3,085,083 in the polymerization systems of perfluorovinyl-ethers in solvent.

U.S. Pat. No. 3,817,960 relates to the preparation and polymerization of perfluorovinylethers of formula: CF₃O(CF₂O)_(n″)CF₂CF₂OCF═CF₂ wherein n″ can range from 1 to 5. The vinylether synthesis is complex. No characterization data on the above properties are reported.

U.S. Pat. No. 3,896,179 relates to the separation of “primary” perfluorovinylether isomers, for example of CF₃CF₂CF₂OCF═CF₂ from the respective “secondary” less stable isomers CF₃(CF₃)CFOCF—═CF₂. The latter are undesired products as regards the polymer preparation and the poor properties of the obtained polymers.

U.S. Pat. No. 4,487,903 refers to the preparation of fluoroelastomeric copolymers using perfluoro vinylethers of formula: CF₂═CF (OCF₂CFY⁰)_(n) ⁰OX² wherein n⁰ ranges from 1 to 4; Y⁰=F, Cl, CF₃, H; X² can be C₁-C₃ perfluoroalkyl, C₁-C₃ ω-hydroperfluoroalkyl, C₁-C₃ ω-chloroperfluoroalkyl. The polymer has a fluorovinylether unit content ranging from 15 to 50% by moles. Said vinylethers give copolymers having at low temperatures properties higher than those of the above mentioned perfluorovinylethers PVE (perfluoropropylvinyl-ether) and MVE type. In this patent it is disclosed for having good properties at low temperature it is required the presence of at least two ether bonds in the side chain adjacent to the double bond. Furthermore from the patent for n⁰ values higher than 4 lt is difficult to purify the monomers and the effect on the T_(g) decrease is lower. Besides the reactivity of the described vinylethers is very low and it is difficult to obtain polymers having a high molecular weight capable to give good elastomeric properties for the mentioned applications. A TFE/perfluorovinylether copolymer (n⁰=2) 31/69% by weight with Tg of −32° C. is exemplified. However the polymer is obtained with very long reaction times (96 hours of polymerization). Also in this case no characterization data of the cured elastomer are given.

EP 130,052 describes the polymerization of perfluorovinylpolyethers (PVPE) which leads to amorphous perfluoropolymers having a T_(g) ranging from −15° to −100° C. In the patent copolymers and terpolymers of TFE and MVE with vinylethers (PVPE) of formula: CF₂═CFO(CF₂CF(CF₃)O)_(n′″)R⁰ _(f′) are described, wherein n′″ ranges from 3 to 30 and R⁰ _(f′) is a perfluoroalkyl. Owing to purification difficulties, the used vinylethers are vinylether mixtures with different n′″ values. According to this patent the most marked effect on the T_(g) decrease is shown when n′″ is equal to or higher than 3, preferably higher than 4. According to the polymerization examples described in said patent the final polymer mass, besides the hot and under vacuum treatment, must then be washed with freon® TF to remove all the unreacteed monomer (PVPE). From the Example it can be seen that the reactivity of all the described monomers (PVPE) is poor.

U.S. Pat. No. 4,766,190 relates to the polymerization of perfluorovinylpolyethers (PVPE) similar to those of U.S. Pat. No. 4,487,903 with TFE and low perfluoropropene percentages, to increase the mechanical properties of the obtained polymers.

U.S. Pat. No. 5,401,818 relates to the preparation of perfluorovinylethers of formula: R¹ _(f)(OCF₂CF₂CF₂)_(m′)—OCF═CF₂ (wherein R¹ _(f) is a C₁-C₃ perfluoroalkyl radical and m′ an integer ranging from 1 to 4) and of the respective copolymers having improved properties at low temperature. The preparation of said perfluorovinylethers takes place by 7 steps, of which some have very low yields and comprising also a perfluorination with elemental F₂. The reactivity of said perfluorovinylethers is anyway low.

Other problems shown by the prior art relate to the low perfluorovinylether reactivity, making necessary the recovery from the reaction raw products of the unreacted monomers (British patent GB 1,514,700), and the stability problems for the polymers having —C(O)F end groups (U.S. Pat. No. 3,635,926). The latter can be further transformed with suitable reactants to increase the polymer stability (EP 178,935).

The perfluorooxyalkylvinylethers are furthermore used to give fluorinated rubbers good properties at low temperatures and in particular to lower the glass transition temperature.

By increasing the perfluorooxyalkylene units, the Tg of the copolymers decreases, but at the same time the vinylether reactivity drastically decreases, making difficult or impossible to obtain polymers having a sufficiently high molecular weight to obtain polymers with good properties. Further the problems previously shown for the recovery of the unreacted monomer from the polymerization raw products or from the polymer itself are still present (U.S. Pat. No. 4,487,903—EP 130,052).

The amorphous TFE copolymers with perfluoromethylvinylether having a T_(g) at about 0° C. or slightly lower (Maskornik, M. et al. “ECD-006 Fluoroelastomer—A high performance engineering material”, Soc. Plast Eng. Tech. Pao. (1974), 20, 675-7).

The extrapolated value of the T for the MVE homopolymer is about −5° C. (J. Macromol. Sci.-Phys., B1 (4), 815-830, December 1967).

Other patents describing vinylethers for obtaining fluoroelastomers are known. See U.S. Pat. No. 6,255,536 and WO 99/48,939.

Patent application EP 1,308,467 describes perfluoroelastomers containing fluoroalkoxyvinylethers of formula CFX_(A)═—CX_(A)OCF₂OR_(A), wherein X_(A)=F, H, R_(A) is C₂-C₆ perfluoroalkyl, perfluorooxyalkyl, or C₅-C₆ cyclic (per)fluoroalkyl. In particular the following perfluoroalkoxyvinylethers are described: CF₂═CFOCF₂OCF₂CF₃ (MOVE 1) and CF₂═CFOCF₂OCF₂CF₂OCF₃ (MOVE 2). In the Examples perfluoroelastomers containing at most about 40% of said perfluoroalkoxyvinylethers are described. The MOVE perfluoroelastomers with TFE contain —COF end groups. See the comparative Examples. To prepare polymeric compositions containing a TFE amount lower than or equal to 60% by moles it is necessary to use long polymerization times. From the industrial point of view this represent a drawback since the productivity is worsened.

Processes to remove or to reduce the —COF or other type of end groups in perfluoropolymers are described in the prior art. See for example patent application EP 1,256,591. The —COF end groups elimination, once the polymer has been obtained, leads to certain application advantages, for example when perfluorinated amorphous polymers are used for optical applications. However the mechanical properties do not improve after this treatment and therefore they do not solve the technical problem i.e. to have available perfluoroelastomers having an improved combination of mechanical and compression set properties in a wide temperature range, at high and at low temperatures.

The need was felt to have availabale perfluoroelastomers having the following combination of properties:

-   -   Tg lower than −10° C., more preferably lower than −20° C., still         more preferably lower than −35° C., in particular lower than         −40° C.;     -   substantially —COF end group free, said end groups being         undetectable by the method indicated afterwards;     -   improved molecular weight, as shown by the higher value of the         intrinsic viscosity;     -   improved mechanical and compression set properties in a wide         temperature range, both at high and at low temperatures;     -   improved productivity of the process for obtaining         perfluoroelastomers, expressed as (polymer Kg)/(hour×litre of         water)

The Applicant has unespectedly and surprisingly found perfluoroelastomers having a surprisingly improved combination of the above mentioned properties.

It is an object of the present invention perfluoroelastomers curable by peroxidic route having a glass transition temperature lower than −10° C., preferably lower than −20° C., more preferably lower than −35° C., in particular lower than −40° C., and having an amount of —COF end group lower than the sensitivity limit of the method described herein: at the end of the polymerization, the polymer is isolated by coagulation by freezing and subsequent defrosting; it is washed twice with demineralizd water and is dried in a stove until a constant weight; the —COF end groups are determined by FT-IR spectroscopy, wherein on a polymer film having a thickness from 50 to 300 micron a scanning between 4000 cm⁻¹ and 400 cm⁻¹ is carried out, the film being then kept for 12 hours in an environment saturated with ammonia vapours and recording the IR spectrum under the same conditions of the initial IR spectrum; elaborating the two spectra by subtracting to the signals of the spectrum of the untreated specimen (initial spectrum) the corresponding ones of the specimen spectrum after exposure to ammonia vapours, drawing the “difference” spectrum, normalized by the following equation: $\frac{``{{Difference}\quad{spectrum}}"}{\left\lbrack {{film}\quad{weight}\quad{(g)/{film}}\quad{area}\quad\left( {cm}^{2} \right)} \right\rbrack};$ the optical densities related to the —COF end groups, reacted with the ammonia vapours, are measured; the optical densities are converted into mmoles/kg of polymer by using the extinction coefficients reported in Table 1, page 73 of the report by M. Pianca et Al. “End groups in fluoropolymers”, J. Fluorine Chem. 95 (1999), 71-84 (herein incorporated by reference); the found values express the concentrations of the residual —COF end groups as mmoles of end groups —COF/Kg of polymer: in the perfluoroelastomer spectrum no bands related to COF groups (1900-1830 cm⁻¹) are detectable, the method sensitivity limit being 0.05 mmoles/Kg.

More particularly the amountof of —COF end groups in the polymer is determined by using the Nicolet® Nexus FT-IR equipment (256 scannings, resolution 2 cm⁻¹).

The perfluoroelastomers according to the present invention preferably comprise also units deriving from bis-olefins of general formula:

-   -   wherein:     -   R₁, R₂, R₃, R₄, R₅, R₆, equal to or different from each other,         are H or C₁-C₅ alkyls;     -   Z is a C₁-C₁₈ linear or branched alkylene or cycloalkylene         radical, optionally containing oxygen atoms, preferably at least         partially fluorinated, or a (per)fluoropolyoxyalkylene radical,         as described in EP 661,304 in the name of the Applicant.

The amount of bis-olefins is generally from 0.01 to 1.0% by moles, preferably from 0.03 to 0.5% by moles, still more preferably from 0.05 to 0.2 moles per 100 moles of the above monomeric units, constituting the perfluoroelastomer structure; the monomer total sum being 100%.

In formula (I), Z is preferably a C₄-C₁₂, more preferably C₄-C₈, perfluoroalkylene radical, while R₁, R₂, R₃, R₄, R₅, R₆ are preferably hydrogen;

-   when Z is a (per)fluoropolyoxyalkylene radical, it can comprise     units selected from the following: -   —CF₂CF₂C—, —CF₂CF(CF₃)O—, —CFX₁O— wherein X₁=F, CF₃, —CF₂CF₂CF₂O—,     —CF₂—CH₂CH₂O—, —C₃F₆O—.

Preferably Z has formula: -(Q)_(p)-CF₂O(CF₂CF₂O)_(m)(CF₂O)_(n)—CF₂—(O)_(p)—  (II) wherein: Q is a C₁-C₁₀ alkylene or oxyalkylene radical; p is 0 or 1; m and n are numbers such that the m/n ratio is between 0.2 and 5 and the molecular weight of said (per)fluoropolyoxyalkylene radical is in the range 500-10,000, preferably 700-2,000.

Preferably Q is selected from:

-   —CH₂OCH₂—; —CH₂O(CH₂CH₂O)CH₂—, s being=1-3

The bis-olefins of formula (I) wherein Z is an alkylene or cycloalkylene radical can be prepared according to what described, for example, by I. L. Knunyants et al. in Izv. Akad. Nauk. SSSR, Ser. Khim., 1964 (2), 384-6. The bis-olefins containing (per)fluoropolyoxyalkylene structures are described in U.S. Pat. No. 3,810,874.

More preferably the bis-olefin has formula: CH₂═CH—(CF₂)_(t0)—CH═CH₂ wherein t0 is an integer from 6 to 10.

The bis-olefin of formula: CH₂═CH—(CF₂)₆—CH═CH₂  (b). is particularly preferred.

The perfluoroelastomers of the invention are cured by peroxidic route. For this reason the invention curable perfluoroelastomers contain preferably iodine and/or bromine, more preferably iodine, in amounts generally between 0.001% and 5% by weight, preferably between 0.01% and 2.5% by weight with respect to the total polymer weight. The iodine atoms can be present in the chain and/or in end position.

To introduce iodine and/or bromine atoms along the chain, the copolymerization of the basic monomers of the fluoroelastomer is carried out with a suitable fluorinated comonomer containing iodine and/or bromine (cure-site monomers), see for example U.S. Pat. No. 4,745,165, U.S. Pat. No. 4,831,085, U.S. Pat. No. 4,214,060, EP 683,149. Said fluorinated comonomer containing iodine can be selected for example from the following compounds:

-   (a) iodo(per)fluoroalkyl-perfluorovinylethers of formula:     I−R_(f)—O—CF═CF₂  (III)     -   wherein R_(f) is a C₁-C₁₂ (per)fluoroalkylene, optionally         containing chlorine and/or ether oxygen atoms;     -   for example: ICF₂—C—CF═CF₂, ICF₂CF₂—O—CF═CF₂,         ICF₂CF₂CF—O—CF═CF₂, CF₃CFICF₂—O—CF═CF₂, and the like; -   (b) iodo-(per)fluoroolefins of formula:     I—R′_(f)—CF═CF₂  (IV)     -   wherein R′_(f) is a C₁-C₁₂ (per)fluoroalkylene, optionally         contining chlorine atoms; for example: iodotrifluoroethylene,         1-iodo-2,2-difluoroethylene,         iodo-3,3,4,4-tetrafluorobutene-1,4-iodo-perfluorobutene-1, and         the like; -   (c) iodo-(per)fluoroolefins of formula:     CHR_(O)═CH-Z_(O)-CH₂CHR_(O)—I  (V)     -   wherein: R_(O) is H or —CH₃; Z_(O) is a C₁-C₁₈ linear or         branched (per)fluoroalkylene radical, optionally containing one         or more oxygen atoms, or a (per)fluoropolyoxyalkylene radical as         above defined.

Other cure-site iodinated comonomers are iodofluoroalkylvinylethers, see U.S. Pat. No. 4,745,165 and U.S. Pat. No. 4,564,662.

Alternatively, or in addition to the iodinated comonomer, the perfluoroelastomer can contain iodine atoms in end position, deriving from a suitable iodinated chain transfer agent introduced in the reaction medium during the polymer preparation, as described in U.S. Pat. No. 4,501,869. Said transfer agents have formula R^(A) _(f)(I)_(x), wherein R^(A) _(f) is a C₁-C₁₂ (per)fluoroalkyl radical, optionally containing chlorine atoms, while x is 1 or 2. Said transfer agents can be selected, for example, from: CF₂ I₂, I(CF₂)₆I, I(CF₂)₄I, CF₂ClI, CF₃CFICF₂I, and the like.

For the iodine introduced as chain end group by addition of iodinated chain transfer agents as above see for example U.S. Pat. No. 4,243,770 and U.S. Pat. No. 4,943,622.

It is also possible to use as chain transfer agents alkaline or alkaline-earth metal iodides, according to patent application EP 407,937.

In combination with the chain transfer agents containing iodine, other known chain transfer agents of the prior art can be used, as ethyl acetate, diethylmalonate, etc.

The iodine amount in end position of the perfluoroelastomer is generally between 0.001% and 3%, preferably between 0.01% and 1% by weight with respect to the fluoroelastomer weight. See U.S. Pat. No. 4,035,565 and U.S. Pat. No. 4,694,045.

Furthermore the curable perfluoroelastomers can contain, alternatively or in combination with iodine, also bromine, in the chain and in end position. The bromine in the chain can be introduced according to known techniques; see for example U.S. Pat. No. 4,035,565, U.S. Pat. No. 4,745,165, EP 199,138; or as end bromine as described in U.S. Pat. No. 4,501,869.

Preferably the perfluoroelastomer contains iodine atoms in the chain and/or in end position.

Optionally the invention perfluoroelastomers comprise in admixture a semicrystalline (per)fluoropolymer, in an amount in percent by weight referred to the total of the dry weight of the mixture perfluoroelastomer+semicrystalline (per)fluoropolymer, from 0% to 70%, preferably from 0% to 50% by weight, still more preferably from 2% to 30% by weight.

With semicrystalline (per)fluoropolymer it is meant a (per)fluoropolymer showing, besides the glass transition temperature Tg, at least one crystalline melting temperature.

The semicrystalline (per)fluoropolymer is constituted of tetrafluoroethylene (TFE) homopolymers, or TFE copolymers with one or more monomers containing at least one unsaturation of ethylene type, in an amount from 0.01% to 10% by moles, preferably from 0.05% to 7% by moles.

Said comonomers having an ethylene unsaturation are both of hydrogenated and fluorinated type. Among those hydrogenated, ethylene, propylene, acrylic monomers, for example methylmethacrylate, (meth) acrylic acid, butylacrylate, hydroxyethylhexylacrylate, styrene monomers, can be mentioned.

Among fluorinated comonomers it can be mentioned:

-   -   C₃-C₈ perfluoroolefins, as hexafluoropropene (HFP),         hexafluoroisobutene;     -   C₂-C₈ hydrogenated fluoroolefins, as vinyl fluoride (VF),         vinylidene fluoride (VDF), trifluoroethylene,         perfluoroalkylethylene CH₂═CH—R_(f), wherein R_(f) is a C₁-C₆         perfluoroalkyl;     -   C₂-C₈ chloro- and/or bromo- and/or iodo-fluoroolefins, as         chlorotrifluoroethylene (CTFE);     -   CF₂═CFOR_(f) (per)fluoroalkylvinylethers (PAVE), wherein R_(f)         is a C₁-C₆ (per)fluoroalkyl, for example CF₃, C₂F₅, C₃F₇;     -   CF₂═CFOX (per)fluoro-oxyalkylvinylethers, wherein X is: a C₁-C₁₂         alkyl, or a C₁-C₁₂ oxyalkyl, or a C₁-C₁₂ (per)fluoro-oxyalkyl         having one or more ether goups, for example         perfluoro-2-propoxy-propyl; fluorodioxoles, preferably         perfluorodioxoles.

PAVEs, in particular perfluoromethyl-, ethyl-, propylvinylether and fluorodioxoles, preferably perfluorodioxoles, are preferred comonomers.

When the perfluoroelastomers of the present invention contain semicrystalline (per)fluoropolymers, mixing is carried out by mixing in the desired ratios the perfluoroelastomer latex with the semicrystalline perfluoropolymer latex and then co-coagulating the obtained mixture as described in U.S. Pat. No. 6,395,834 and U.S. Pat. No. 6,310,142.

Alternatively the semicrystalline (per)fluoropolymer can be polymerized and then the perfluoroelastomer is let polymerize on the (per)fluoropolymer particles. It is thus obtained a core-shell structure.

The Applicant has found that when the —COF end group amount in the perfluoropolymer, after polymerization, is substantially absent according to the above analysis method, it is obtained the best combination of mechanical and compression set properties in a wide temperature range, both at high and at low temperatures.

It is a further object of the present invention compositions comprising:

-   -   perfluoroelastomers of the present invention, having an amount         of —COF end groups lower than 0.05 mmoles/Kg and Tg as above         defined, and     -   perfluoroelastomers obtainable from polymers containing an         amount of —COF end group higher than 0.05 mmoles/Kg;         provided that the amount of perfluoroelastomer of the present         invention is at least 5-10% by weight, preferably 20-40% by         weight, more preferably 50% by weight, with respect to the total         weight of the perfluoroelastomers in the composition.

These compositions can be obtained in various ways. For example, when monomers giving —COF end groups are used in polymerization to obtain the improved properties according to the present invention it is carried out a part of polymerization of monomers in the absence of those giving —COF end groups, so as to obtain a polymer aliquot substantially —COF end group free which allows to obtain the combination of the above properties. For example the polymer obtained in the polymerizat-ion part carried out in the absence of monomers giving —COF end groups must be at least 5-10% by weight, preferably 20-40% by weight, more preferably 50% by weight, with respect to the final polymer weight. An alternative process is that to mix the polymers of the present invention substantially —COF end group free with polymers containing —COF in the above indicated ratios.

The perfluoroelastomers containing —COF end groups in an amount higher than 0,05 mmoles/Kg comprise comonomers selected from the following:

-   -   perfluorodioxoles, preferably having the following formula:     -   wherein     -   Y═F, ORf₁, Rf₁ being a C₁-C₅ perfluoroalkyl, preferably Rf₁ is         CF₃;     -   X₁ and X₂, equal to or different from each other, are selected         between F and CF₃, preferably F;     -   Z₁ is selected between F, Cl, preferably F;     -   perfluoroalkylvinylethers of formula CF₂═CFORf wherein Rf is a         C₃ perfluoroalkyl;     -   CF₂═CFOXa perfluorooxyalkylvinylethers, wherein Xa is C₃-C₁₂         perfluorooxyalkyl having one or more ether groups, for example         perfluoro-2-propoxy-propyl;     -   perfluorovinylethers (MOVE) of general formula         CFX_(AI)═CX_(AI)OCF₂OR_(AI) (A-I) wherein R_(AI) is a C₂-C₆         linear, branched or C₅-C₆ cyclic perfluoroalkyl group, or a         C₂-C₆ linear or branched when possible perfluorooxyalkyl group         containing from one to three oxygen atoms; X_(AI)=F; the         compounds of general formula: CFX_(AI)═CX_(AI)OCF₂OCF₂CF₂Y_(AI)         (A-II) wherein Y_(AI)=F, OCF₃ are preferred; in particular         (MOVE 1) CF₂═CFOCF₂OCF₂CF₃ (A-III) and (MOVE 2)         CF₂═CFOCF₂OCF₂CF₂OCF₃ (A-IV).

The curable perfluoroelastomers of the invention preferably comprise the following monomers (percent by moles):

-   A) from 1% to 100%, preferably from 5% to 100%, of the monomer of     formula:     CF₂═CFOCF₂OCF₃  (a) -   B) one or more perfluorinated comonomers having at least one     ethylene type unsaturation, from 0% to 99%, preferably from 0 to     95%; -   the sum of the molar monomer percentages being 100%; with the     proviso that when comonomer B) is TFE or the mixture of     comonomers B) contains TFE, the TFE amount must be such that the     polymer is elastomeric; the —COF end groups amount being as above.

Said perfluoroelastomers preferably contain one bis-olefin.

More particularly the amount of —COF end groups in the polymer is determined by using the Nicolet® Nexus FT-IR apparatus (256 scannings, resolution 2 cm⁻¹).

Elastomeric polymers, according to the present invention are polymers which at the DSC (differential scanning calorimetry) do not show melting peaks, since the crystalline part is substantially absent.

When the copolymer does not contain other comonomers (B) besides TFE, the monomer amount of formula (a) is generally higher than about 15% by moles to obtain elastomeric polymers.

Comonomers B) are selected from the following:

-   -   C₂-C₈ perfluoroolefins, for example TFE, hexafluoropropene;     -   perfluoroalkylvinylethers of formula CF₂═CFORf wherein Rf is a         C₁-C₂ perfluoroalkyl, preferably Rf=CF₃.

Tetrafluoroethylene (TFE) and/or perfluoromethylvinylether (MVE) are preferred comonomers B).

Preferred compositions (in % by moles) are the following, the sum of the monomer molar percentages being 100%; more preferably said compositions contain a bis-olefin:

-   monomer of formula (a): 100%; -   preferably monomer of formula (a): 99.0%-99.99% bis-olefin of     formula (b) 1%-0.01%; more preferably monomer of formula (a):     99.90-99.99%, bis-olefin of formula (b) 0.1-0.01%; -   monomer of formula (a): 15-40%, TFE: 60-85%; preferably monomer of     formula (a): 18-30%, TFE: 69-81.99%, bis-olefin of formula (b)     1-0.01%; -   monomer of formula (a): 40-99%, TFE: 1-60%; preferably monomer of     formula (a): 39-98.99%, TFE 1-60%, bis-olefin of formula (b)     1-0.01%; -   monomer of formula (a): 5-40%, MVE: 5-30%, TFE: 50-85%; preferably     monomer of formula (a): 5-40%, MVE: 5-30%, TFE: 50-85%, bis-olefin     of formula (b) 1-0.01%; -   monomer of formula (a): 40-99%, MVE: 5-30%, TFE: 1-60%; preferably     monomer of formula (a): 40-99%, MVE: 5-30%, TFE: 1-60%, bis-olefin     of formula (b) 1-0.01%.

As said, the perfluoroelastomers of the invention show an improved combination of the above properties.

The perfluoroelastomers of the present invention show a good elastic behaviour at low temperatures, as for example shown by the TR10 and TR70 values (ASTM D 1329).

The perfluoroelastomers of the present invention compared with the perfluoroelastomers of the prior art having a Tg lower than −10° C., the comparison being carried out with the same Tg, show improved mechanical and compression set properties and a higher resistance at high temperatures. In a comparison carried out with the perfluoromethylvinylether based perfluoroelastomers (the most largely marketed perfluoroelastomers) the perfluoroelastomers of the present invention show a lower Tg and improved properties at low temperatures, as shown by the TR values.

The Applicant has unexpectedly and surprisingly found that the perfluoroelastomers of the present invention are obtained with high polymerization kinetics, therefore it is possible to obtain homopolymers and copolymers having a high molecular weight. The perfluoroelastomers of the present invention are obtainable with high yields and therefore the recovery of the unreacted monomers is useless, at the end of the polymerization. This allows to simplify the production plant, since the expensive recovery methods of unreacted monomers are not necessary.

The preparation of perfluoroelastomers of the present invention is carried out by polymerization of the monomers in aqueous emulsion in the presence of an emulsion, dispersion or microemulsion of perfluoropolyoxyalkylenes, according to U.S. Pat. No. 4,789,717 and U.S. Pat. No. 4,864,006. Preferably the synthesis is carried out in the presence of a perfluoropolyoxyalkylene microemulsion.

According to well known methods of the prior art, radical initiators, for example alkaline or ammonium persulphates, perphosphates, perborates or percarbonates, optionally in combination with ferrous, cupreous or silver salts, or other easily oxidizable metals, are used. In the reaction medium also surfactants of various kind are optionally present, among which fluorinated surfactants of formula: R³ _(f)—X_(k) ⁻M⁺ are particularly preferred, wherein R³ _(f) is a C₅-C₁₆ (per)fluoroalkyl chain or (per)fluoropolyoxyalkyl chain, X_(k) ⁻ is —COO⁻ or —SO₃ ⁻, M⁺ is selected among: H⁺, NH₄ ⁺, or an alkaline metal ion. Among the most commonly used we remember: ammonium perfluorooctanoate, (per)fluoropolyoxyalkylenes ended with one or more carboxylic groups, etc. See U.S. Pat. No. 4,990,283 and U.S. Pat. No. 4,864,006.

The polymerization reaction is generally carried out at temperatures between 25° C. and 150° C., at a pressure between the atmospheric pressure up to 10 MPa.

In alternative or in combination with the chain transfer agents containing iodine and/or bromine, other chain transfer agents known in the prior art, as ethyl acetate, diethylhylmalonate, ethane, etc., can be used.

As said, the perfluoroelastomers of the present invention are cured by peroxidic route.

In the peroxidic curing, preferably the perfluoroelastomer contains in the chain and/or in end position to the macromolecule iodine and/or bromine atoms.

To the curing blend the following components are added:

-   -   peroxides capable to generate radicals by heating, for example:         dialkylperoxides, in particular di-terbutyl-peroxide and         2,5-dimethyl-2,5-di(terbutylperoxy)hexane; dialkylarylperoxides         as for example dicumyl peroxide; dibenzoyl peroxide; diterbutyl         perbenzoate; di[1,3-dimethyl-3-(terbutylperoxy)butyl]-carbonate.         Other peroxidic systems are described, for example, in European         patent applications EP 136,596 and EP 410,351.

The peroxide amount is generally from 0.5% to 10% by weight with respect to the polymer, preferably 0.6%-4% by weight;

-   -   curing coagents, in amounts generally between 0.5 and 10%,         preferably between 1 and 7%, by weight with respect to the         polymer; among them, bis-olefins of formula (I);         triallyl-cyanurate, triallyl-isocyanurate (TAIC),         tris(diallylamine)-s-triazine; triallylphos-phite;         N,N-diallyl-acrylamide; N,N,N′,N′-tetraallyl-malonamide;         tri-vinyl-isocyanurate; and 4,6-tri-vinyl-methyltrisiloxane,         etc., are commonly used: TAIC and the bis-olefin of formula         CH₂═CH—(CF₂)₆—CH═CH₂;     -   are particularly preferred; optionally     -   a metal compound, in amounts between 1 and 15%, preferably from         2 to 10% by weight with respect to the polymer, selected from         divalent metal oxides or hydroxides, as for example Mg, Zn, Ca         or Pb, optionally combined with a weak acid salt, as stearates,         benzoates, carbonates, oxalates or phosphites of Ba, Na, K, Pb,         Ca;     -   other conventional aditives, as mineral fillers, semicrystalline         fluoropolymers in powder, pigments, antioxidants, stabilizers         and the like.

The semicrystalline (per)fluoropolymers, optional components of the present invention, are prepared according to the emulsion or microemulsion polymerization methods above described for the perfluoroelastomers of the invention.

The monomer of formula (a) CF₃OCF₂OCF═CF₂ used in the polymers of the present invention can be prepared by a synthesis comprising the following steps:

-   I obtainment of the fluoroformate CF₃OCOF; -   II reaction in liquid phase of the fluoroformate CF₃OCOF with     elemental fluorine and olefinic compounds having formula:     CAF═CA′F  (IV)     -   for obtaining the fluorohalogenether of formula:         CF₃OCF₂OCFACF₂A′  (V)     -   wherein A and A′, equal to or different the one from the other,         are H, Cl or Br, with the proviso that both are not H; the         fluorination reaction temperture can range from −120° C. to −20°         C., preferably from −100° C. to −40° C.;     -   optionally one operates in the presence of a perhalogenated         solvent, liquid and inert under the reaction conditions; the         fluorine can optionally be diluted with an inert gas, e.g.         nitrogen or helium; -   III removal of the substituents A and A′ from the     fluorohalogenether (V) by a dehalogenation when A and A′ are     halogen, or a dehydrohalogenation when one of A or A′ is hydrogen     and the other is halogen; -   the fluoroformate CF₃OCOF of step I can be prepared with high     conversion and selectivity by thermal reaction, in gaseous phase, of     CF₃OF (fluoroxyperfluoromethane) with CO in a reactor maintained at     temperatures between 80° C. and 250° C., preferably between 120° C.     and 230° C., still more preferably between 150° C. and 200° C.

The dehalogenation or dehydrohalogenation reactions used are well known in the prior art.

The molar ratio CF₃OF/CO is between 0.1 and 10, preferably between 0.2 and 5, more preferably between 0.5 and 2.

The perhalogenated solvent optionally used in step II, is preferably an organic compound containing fluorine and/or chlorine, optionally one or more oxygen atoms in the chain and/or aminic groups as the end group.

When the perhalogenated solvent is perfluorinated, it can for example be selected among perfluorocarbons, perfluoroethers, perfluoropolyethers, perfluoroamines, or respective mixtures.

The reaction mixture containing CF₃OCOF of step I can be directly fed, without separation of the mixture components, into the other reactor for the reaction of step II. The process for obtaining the monomer of step I starting from CF₃OF resulted particularly simple and effective. As said, the CF₃OF conversion and the selectivity to CF₃OCOF are high (see the Examples).

In step I, by increasing the reaction temperature in the range 80°-250° C., the conversion increases and, at the same time, a high selectivity is substantially maintained.

Alternatively, the CF₃OCOF of step I can be prepared by photochemical route, in liquid phase, by feeding the two reactants, as above indicated, into a reactor equipped with a mercury high pressure UV lamp, contained in a cooled quartz sheath, immersed in the reaction mixture, at temperatures comprised between 0° C. and 100° C., preferably between 20° C. and 50° C.,

It has been found that the formation reaction of the fluoroformate by photochemical route has a high selectivity, and that higher yields are obtained compared with the same reaction carried out in gaseous phase.

The reaction by photochemical route is carried out in the presence of an inert perfluorinated solvent, liquid under the reaction conditions.

Preferably the perfluorinated solvent is selected from perfluorocarbons, perfluoropolyethers, perfluorinated tertiary amines, fluorochlorocarbons, or mixtures thereof.

When the CF₃OF conversion is not quantitative, the gaseous flow leaving the reactor contains a mixture formed of the reaction product together with unconverted CO and CF₃OF The latter can be removed by passing the gaseous flow into a cold trap containing a fluorinated olefin, for example CFCl=CFCl; then by fractional distillation CF₃OCOF is separated.

Alternatively the gaseous reaction mixture containing the reaction products formed in step I is cooled to condensate the fluoroformate separating CF₃OF and CO which can be recycled into the reactor.

Preferably step I is carried out by reacting the fluorooxyperfluoromethane and carbon monoxide at temperatures from 80° C. to 250° C.

Preferably the reactor used in step I is made of glass, inert perfluorinated plastics, as for example PTFE, PFA, metal alloys, for example AISI 316, preferably coated with glass or perlfuorinated plastics. More preferably, as materials, glass or fluorinated plastics are used.

The perfluoroelastomers of the present invention, as said, show an improved combination at high temperatures of mechanical properties, in particular modulus, stress at break and elongation at break, of elastomeric properties as shown by the compression set, and of thermal resistance; and contemporaneously they show an improved combination of the above properties even at low temperatures.

The perfluoroelastomers of the present invention are usable to obtain manufactured articles for temperatures lower than −10° C. up to 300° C., having improved mechanical and elastomeric properties.

The following Examples illustrate with non limitative purposes the present invention.

EXAMPLES

Analytical Methods

Determination of the Polymer Tg

The Tg has been determined by DSC analysis according to the ASTM D 3418 method. The Tg values reported in the Examples are the mid-point Tg.

Determination of the Intrinsic Viscosity

The intrinsic viscosity has been determined in perfluoroheptane at the temperature of 30° C.

Determination of the —COF Polar End Groups

At the end of the polymerization, the polymer is isolated by coagulation by freezing at −20° C. and subsequent defrosting at room temperature until obtaining a slurry wherein the polimer deposits on the bottom; it is washed twice with demineralized water and it is dried in a stove at 90° C. until a constant weight (about 12 hours); the —COF end groups are determined by FT-IR spectroscopy, by using the Nicolet® Nexus FT-IR equipment (256 scannings, resolution 2 cm⁻¹), wherein on a polymer film having a thickness from 50 to 300 micron a scanning between 4000 cm⁻¹ and 400 cm⁻¹ is initially carried out, the film being then kept for 12 hours in an environment saturated with ammonia vapours, and recording at the end the IR spectrum under the same conditions of the initial IR spectrum; elaborating the two spectra by subtracting to the signals of the spectrum related to the untreated specimen (initial spectrum) the corresponding signals of the specimen spectrum after exposure to ammonia vapours, drawing the “difference” spectrum, normalized by the following equation: $\frac{``{{Difference}\quad{spectrum}}"}{\left\lbrack {{film}\quad{weight}\quad{(g)/{film}}\quad{area}\quad\left( {cm}^{2} \right)} \right\rbrack};$ the optical densities related to the —COF end groups, reacted with the ammonia vapours, are measured; the optical densities are converted into mmoles/kg of polymer by using the molar extinction coefficient of the —COF group at 1884 cm⁻¹, equal to 215 litres/(moles×cm), as reported in Table 1, page 73 of the report by M. Pianca et Al. “End groups in fluoropolymers”, J. Fluorine Chem. 95 (1999), 71-84 (herein incorporated by reference); the found values express the concentrations of the residual —COF end groups as mmoles of end groups —COF/Kg of polymer: in the perfluoroelastomer spectrum no bands related to COF groups (1900-1830 cm⁻¹) are detectable, the method sensitivity limit being 0.05 mmoles/Kg. Mooney Viscosity Determination

The Mooney viscosity (1+10′ at 121° C.) is determined according to the ASTM D 1646 method.

Compression Set Determination

The Compression Set is determined according to the ASTM D 395 method.

TR Determination

The TR Test is determined according to the ASTM D 1329 method.

Example A

Preparation of CF₃OCOF by Thermal Reaction at 170° C. in Glass Reactor

A tubular glass reactor is used, having an inner diameter of 55.6 mm and length of 510 mm, filled with 6×6 glass Raschig rings (free internal volume 842 ml), maintained thermostated by electric resistances.

In the reactor, maintained at the temperature of 170° C., a gaseous flow of CF₃OF (1.5 litres/hour), synthesized as described in U.S. Pat. No. 4,400,872 and, contemporaneously, a CO flow (1.5 litres/hour), are fed for 5 hours. The flow coming out from the reactor is continuously analyzed by online gaschromatographic analysis.

The flow coming out from the reactor is condensed, except CO, in a trap maintained at −110° C. containing 15 g of CFCl=CFCl (A 1112), so that the residual CF₃OF reacts with the olefin to give CF₃OCFClCF₂Cl.

After fractional distillation of the resulting mixture, 33.9 g of CF₃OCOF pure at 99.8% (molar yield on the fed CF₃OF 76.5%); 12.3 g of CF₃OCFClCF₂Cl; 3.4 g of COF₂ are obtained.

The conversion is 84.5% and the selectivity 90%, calculated on the fed CF₃OF

Example B

Preparation of CF₃OCOF by Thermal Reaction at 170° C. in PTFE Reactor

A PTFE tubular thermostated reactor is used, having an internal diameter of 4 mm and length of 13.2 m.

A gaseous flow of CF₃OF (1.5 litres/hour) and, contemporaneously, a flow of CO (2.0 litres/hour) are fed into the reactor, maintained at the temperature of 170° C.

The flow coming out from the reactor, analyzed by gaschromatography, has the following molar composition: 7.3% CF₃OF, 54.2% CF₃OCOF, 9.1% COF₂ and 29.4% CO.

Example C

Preparation of CF₃OCOF by Thermal Reaction at 120° C. in PTFE Reactor

A gaseous flow of CF₃OF (1.5 litres/hour) and, contemporaneously, a flow of CO (2.0 litres/hour) are fed for 6 hours into the same reactor used in the Example B, maintained at the temperature of 120° C. The flow coming out from the reactor is analyzed by gaschromatography and has the following molar composition, leaving out CO in excess: 86.7% CF₃OF, 13.3% CF₃OCOF.

The flow coming out from the reactor is condensed, except CO, in a trap maintained at −110° C. containing 50 g of A 1112, so that the residual CF₃OF reacts with the olefin.

After fractional distillation of the resulting mixture, 6.8 g of CF₃OCOF having a 99% purity are obtained.

The selectivity is 98%, calculated on the converted CF₃OF The conversion is 13.0%.

Example D

Preparation of CF₃OCOF by Thermal Reaction at 170° C. in AISI 316 Reactor

An AISI 316 tubular thermostated reactor is used, having an internal diameter of 4 mm and length of 11.3 m.

A gaseous flow of CF₃OF (1.5 litres/hour) and, contemporaneously, a flow of CO (1.5 litres/hour) are fed for 6 hours into the reactor, maintained at the temperature of 170-° C. The gaseous flow coming out from the reactor is condensed in a trap maintained at −110° C. containing 30 g of A 1112.

After fractional distillation of the trap content, 31.2 g of CF₃OCOF pure at 99%, 31.8 g of fluorohalogenether and 3.7 g of COF₂ are obtained. The conversion is 66.6% and the selectivity is 86.5%.

Example E

Preparation of CF₃OCOF by Photochemical Reaction

500 g of a perfluoropolyether Galden®LS-165 are fed into a 300 ml cylindrical glass reactor, equipped with stirrer and UV lamp Hanau TQ 150, with 150 W power and optical route 1 cm. Then 2.0 litres/hour of CF₃OF diluted with 3.0 litres/hour of He, and 2.0 litres/hour of CO are fed contemporaneously for 5 hours.

The gases coming out from the reactor are condensed in a trap maintained at −110° C. containing 30 g of A 1112. After fractional distillation of the condensed mixture, 22.9 g of CF₃OCOF pure at 99%, 41.8 g of fluorohalogenether CF₃OCFClCF₂—Cl, 5.8 g of COF₂, 5.4 g of trifluoromethyl carbonate are obtained.

The CF₃OF conversion is 60.5%. The selectivity is 63.6%.

Example F

Obtainment of the Monomer of Formula (a) by Reaction of CF₃O—COF with Elemental Fluorine and a Fluoroolefin of Formula CFCl=CFCl and Subsequent Dehalogenation of the Fluorohalogenether

20 g of CFCl=CFCl (A 1112), 30 g of CF₃OCOF obtained as in the Example A are transferred in a 50 ml glass reactor. The solution formed is maintained at −100° C. and fluorine diluted with nitrogen is bubbled at a flow of 1 litre/hour.

The mass balance at the end of the reaction is 92%, the ¹⁹F-NMR analysis on the reaction raw product (52 g) shows that the fluoroformate conversion is 54% and the selectivity to give the fluorohalogenether CF₃OCF₂OCFClCF₂Cl is 93%. The unreacted fluoroformate is removed from the reaction raw product by adding water, under stirring. It is let reach 25° C., the organic phase is recovered and dried over MgSO₄. The mixture is filtered and the obtained residue is distilled and the fraction boiling at 74° C. of 31.8 g corresponding to the fluorohalogenether having 99% purity is recovered.

The fluorohalogenether dehalogenation is carried out by using an 1 litre flask equipped with mechanical stirrer, thermometer, funnel dropping, distillation column and trap at −78° C. 450 ml of dimethylformamide (DMF), 62 g of zinc in powder and 8.3 g of ZnCl₂ are fed into the flask. The temperature in the suspension is brought to 80° C. and 150 g of the fluorohalogenether isolated in the previous reaction are added. When the addition is over, the mixture is let react for one hour. At the end the temperature is gradually increased up to 120° C. and it is let react still for one hour. Lastly it is disconnected and 106 g of the monomer of formula (a) CF₃OCF₂OCF═CF₂ having 99% purity (boiling point 23° C.) are recovered therefrom.

Example 1

Preparation of the Microemulsion

The microemulsion is obtained by mixing the following ingredients in the amounts indicated hereinafter to prepare one litre of microemulsion:

-   -   220.7 ml of a perfluoropolyoxyalkylene having acid end group         with average molecular weight 600, of formula:         CF₂ClO(CF₂—CF (CF₃)°)_(n)(CF₂O)_(m)CF₂COOH     -   wherein n/m=10;     -   220.7 ml of an aqueous solution of NH₃ at 30% by volume;     -   427.6 ml of demineralized water;     -   131 ml of Galden® D02, having average molecular weight 450, of         formula:         CF₃O(CF₂—CF (CF₃)O)_(n)(CF₂O)_(m)CF₃     -   wherein n/m=20.

Example 2

Homopolymer of the Monomer of FORMULA (a)

0.03 l of demineralized water, 1.5 ml of the microemulsion of the Example 1, and 12 g of the monomer of formula (a) are introduced in sequence into a 0.1 l (litres) glass autoclave, equipped with magnetic stirring, after vacuum has been made by oil pump. The autoclave is heated to 42° C. Then 0.1 g of ammonium persulphate are introduced. The reactor is maintained at 42° C. for 170 h and then cooled. The obtained latex is degassed. The latex is coagulated by freezing and subsequent defrosting. In this way the polymer is separated from the aqueous phase; it is washed twice with demineralized water and dried in a stove at 100° C. for 8 h.

About 11 g of polymer equal to a conversion of 92% of the fed monomer of formula (a) are obtained. The polymer Tg is −39.4° C. The intrinsic viscosity measured at 30° C. in perfluoroheptane (Galden® D80) is equal to 30.5 cc/g. By IR analysis it is found that the —COF end groups in the polymer are lower than the method sensitivity limit.

Conversions of about 69% of the monomer of formula (a) are obtained with lower polymerization times.

Example 3

Copolymer Monomer of formula (a)/TFE 63/37 (% by Moles Ratio)

20 ml of demineralized water, 1 ml of microemulsion prepared in the Example 1 are introduced in sequence into a 42 ml steel autoclave, equipped with magnetic stirring, after vacuum has been made by oil pump. 10 g of the monomer of formula (a) are added and the autoclave is heated to 80° C. TFE is introduced into the reactor until bringing the pressure to 1.0 MPa. Then 4 mg of ammonium persulphate are introduced. The reaction pressure is maintained constant by addition of TFE at every pressure decrease equal to 0.01 MPa.

The reaction ends after 4 h. The obtained latex is degassed. The latex is coagulated by freezing and subsequent defrosting. In this way the polymer is separated from the aqueous phase; it is washed twice with demineralized water and dried in a stove at 90° C. for 4 h. 5.3 g of polymer equal to 43% of the fed monomer of formula (a) are obtained. The polymer Tg is −42.5° C. (midpoint) and −48.4° C. (onset). The intrinsic viscosity measured at 30° C. in perfluoroheptane (Galden® D80) is equal to 17.0 cc/g.

By NMR analysis the polymer composition is determined; it contains 63% by moles of the monomer of formula (a). By IR analysis it is found that the —COF end groups in the polymer are lower than the method sensitivity limit.

Example 4 (Comparative)

Copolymer MOVE 1/TFE 23/77 (% by moles ratio)

20 ml of demineralized water, 1 ml of microemulsion prepared in the Example 1 are introduced in sequence into a 42 ml steel autoclave, equipped with magnetic stirring, after vacuum has been made by oil pump. 10 g of MOVE 1 are added and the autoclave is heated to 80° C. TFE is introduced into the reactor until bringing the pressure to 1.0 MPa. Then 4 mg of ammonium persulphate are introduced. The reaction pressure is maintained constant by addition of TFE at every pressure decrease equal to 0.01 MPa.

The reaction ends after 4 h. The obtained latex is degassed. The latex is coagulated by freezing and subsequent defrosting. In this way the polymer is separated from the aqueous phase; it is washed twice with demineralized water and dried in a stove at 90° C. for 4 h. 4.0 g of polymer with a conversion of 18% of MOVE 1 with respect to the fed amount are obtained. The polymer Tg is −21.0° C. (midpoint) and −31° C. (onset).

By NMR analysis it is determined the polymer composition which contains 23% by moles of MOVE 1. By IR analysis it is determined a —COF end group content in the polymer equal to 0.25 mmoles/kg.

Example 5

Copolymer Monomer of Formula (a)/HFP

20 ml of demineralized water, 1 ml of microemulsion prepared in the Example 1 are introduced in sequence into a 42 ml steel autoclave, equipped with magnetic stirring, after vacuum has been made by oil pump. 9 g of the monomer of formula (a) are added and the autoclave is heated to 80° C. HFP is introduced into the reactor until bringing the pressure to 1.5 MPa. Then 4 mg of ammonium persulphate are introduced. The reaction pressure is maintained constant by addition of HFP at every pressure decrease equal to 0.01 MPa.

The reaction ends after 4 h. The obtained latex is degassed. The latex is coagulated by freezing and subsequent defrosting. In this way the polymer is separated from the aqueous phase; it is washed twice with demineralized water and dried in a stove at 90° C. for 4 h. 0.5 g of polymer are obtained.

The IR analysis confirms that the obtained polymer is a copolymer based on the monomer of formula (a) with a small amount of HFP (<5% by moles).

Example 6 (Comparative)

Copolymer MOVE 1/HFP

20 ml of demineralized water, 1 ml of microemulsion prepared in the Example 1 are introduced in sequence into a 42 ml steel autoclave, equipped with magnetic stirring, after vacuum has been made by oil pump. 9 g of MOVE 1 are added and the autoclave is heated to 80° C. HFP is introduced into the reactor until bringing the pressure to 1.5 MPa. Then 4 mg of ammonium persulphate are introduced.

The reaction ends after 4 h. The reactor content is degassed and then coagulation is carried out by freezing and subsequent defrosting. No polymer presence is observed. Then MOVE 1 in the adopted conditions is not capable to copolymerize with HFP.

Example 7 (Comparative)

Homopolymer MOVE 1

0.03 l of demineralized water, 1.5 ml of microemulsion of the Example 1 and 9 g of MOVE 1 are introduced in sequence into a 0.1 l (litres) glass autoclave, equipped with magnetic stirring, after vacuum has been made by oil pump. The autoclave is heated to 42° C. Then 0.1 g of ammonium persulphate are introduced. The reaction is maintained at 42° C. for 170 h and then it is cooled.

The obtained latex is degassed. The latex is coagulated by freezing and subsequent defrosting. In this way the polymer is separated from the aqueous phase; it is washed twice with demineralized water and dried in a stove at 100° C. for 8 h.

About 6.2 g of polymer equal to a conversion of 69% of fed MOVE 1 are obtained. The polymer Tg is −31.6° C. The intrinsic viscosity measured at 30° C. in perfluoroheptane (Galden® D80) is equal to 16.5 cc/g. By IR analysis it is found that the —COF end groups in the polymer are 0.35 mmoles/kg.

Example 8

Copolymer Monomer of formula (a)/TFE 64/36 (% by Moles Ratio) Containing Bis-Olefin

20 ml of demineralized water, 1 ml of microemulsion prepared in the Example 1 are introduced in sequence into a 42 ml steel autoclave, equipped with magnetic stirring, after vacuum has been made by oil pump. 10 g of the monomer of formula (a) are added and the autoclave is heated to 80° C. 0.01 g of bis-olefin of formula CH₂═CH—(CF₂)₆—CH═CH₂ dissolved in 0.1 g of Galden D02 are introduced and the pressure in the reactor is brought to 1.0 MPa with TFE. Then 4 mg of ammonium persulphate are introduced. The reaction pressure is maintained constant by addition of TFE at every pressure decrease equal to 0.01 MPa.

The reaction ends after 4 h. The obtained latex is degassed. The latex is coagulated by freezing and subsequent defrosting. In this way the polymer is separated from the aqueous phase; it is washed twice with demineralized water and dried in a stove at 90° C. for 4 h. 5.5 g of polymer equal to 45% of the fed monomer of formula (a) are obtained. The polymer Tg is −44.0° C. (midpoint) and −50,0° C. (onset). The intrinsic viscosity, measured at 30° C. in perfluoroheptane (Galden® D80) is equal to 45.0 cc/g.

By NMR analysis the polymer composition is determined; it contains 64% by moles of the monomer of formula (a). By IR analysis it is found that the —COF end groups in the polymer are lower than the method sensitivity limit.

Comments to Examples 23, 5 and 8 According to the Invention and to the Comparative Examples 4, 6 and 7

The homopolymer of monomer (a) (example 2) over the homopolymer of MOVE 1 (example 7 comparative) shows the following improved properties:

-   -   an higher intrinsic viscosity, therefore an higher molecular         weight;     -   absence of —COF end groups;     -   a lower Tg.

In the polymerization with other comonomer(s), monomer (a) shows a much higher reactivity than MOVE 1. Under similar polymerization conditions and using TFE as comonomer, in example 3 lt is obtained a polymer containing 63% moles of monomer (a), in comparative example 4 the content of MOVE 1 in the copolymer is 23% moles. Under similar polymerization conditions and using HFP as comonomer (see example 5) a copolymer of monomer (a) wherein the content of HFP is <5% moles was obtained, in comparative example 6 the copolymer was not even formed.

The peculiar properties of the copolymers containing monomer (a) are also shown by the Tg values. The copolymers of monomer (a) and TFE of examples 3 and 8, show a Tg of 42.5° C. and 44.0° C. respectively. It must be noted that these Tg values are lower than the Tg of the homopolymer of monomer (a) (example 2) and of the homopolymer of the comonomer TFE.

Example 9

Copolymer Monomer (a)/TFE 31/69 (Molar Ratio)

In a 5 lt autoclave, equipped with stirrer working at 630 rpm, there were introduced, after evacuation, 3.5 lt of demineralized water and 35 ml of microemulsion of perfluoropolyoxyalkylenes previously obtained as in example 1. The autoclave was then heated up to 70° C. and maintained at said temperature for the whole reaction. The following mixture of monomers was then fed: tetrafuoroethylene (TFE) 70% by moles, monomer (a) 30% by moles, so as to bring the pressure up to 0.7 MPa. in the autoclave there were then introduced: 0.5 gr of ammonium persulphate (APS) as initiator; 3.29 gr of 1,4-diiodoperfluorobutane (C₄F₈I₂) as polymer chain transfer agent; 1.5 gr of a bis-olefin of formula CH₂═CH—(CF₂)₆—CH═CH₂; the addition of the bis-olefin was carried out in 20 aliquots, each of 0.075 gr, starting from the beginning of the polymerization and for every 5% increase in the monomer conversion. The pressure of 0.7 MPa was maintained constant for the whole polymerization by feeding a mixture formed by: tetrafuoroethylene (TFE) 60% by moles, monomer (a) 40% by moles. After 210 minutes of reaction, corresponding to 100% of the monomer conversion, the autoclave was cooled and the latex discharged. The so obtained latex is coagulated with a solution of aluminum sulphate (6 gr of Al₂(SO₄)₃ for each litre of latex) and dried at 90° C. in an air circulating over for 16 hours. 594 gr of polymer are obtained.

By ¹⁹F-NMR analysis of the polymer dissolved in hot C₆F₆ it was found that the molar percentage of monomer (a) in the polymer is 31,2%. The T_(g), determined by DSC is −31.2° C. The Mooney viscosity (ML(1+10′ at 121° C.)) determined according to the ASTM D 1646 method is 12 MU. The mechanical properties are shown in Table 1.

Example 10

Copolymer Monomer (a)/TFE 47/53 (Molar Ratio)

In a 5 lt autoclave, equipped with stirrer working at 630 rpm, there were introduced, after evacuation, 3.5 lt of demineralized water and 35 ml of microemulsion of perfluoropolyoxyalkylenes previously obtained as in example 1. The autoclave was then heated up to 70° C. and maintained at said temperature for the whole reaction. The following mixture of monomers was then fed: tetrafuoroethylene (TFE) 38% by moles, monomer (a) 62% by moles, so as to bring the pressure up to 0.7 MPa. In the autoclave there were then introduced: 0.5 gr of ammonium persulphate (APS) as initiator; 3.29 gr of 1,4-diiodoperfluorobutane (C₄F₈I₂) as polymer chain transfer agent; 1.5 gr of a bis-olefin of formula CH₂═CH—(CF₂)₆—CH═CH₂; the addition of the bis-olefin was carried out in 20 aliquots, each of 0.075 gr, starting from the beginning of the polymerization and for every 5% increase in the monomer conversion. The pressure of 0.7 MPa was maintained constant for the whole polymerization by feeding a mixture formed by: tetrafuoroethylene (TFE) 60% by moles, monomer (a) 40% by moles. After 278 minutes of reaction, corresponding to 100% of the monomer conversion, the autoclave was cooled and the latex discharged. The so obtained latex was coagulated as in example 9. 574 gr of polymer were obtained.

By ¹⁹F-NMR analysis of the polymer dissolved in hot C₆F₆ it was found that the molar percentage of monomer (a) in the polymer is 47%. The T_(g), determined by DSC, is −37.8° C. The Mooney viscosity (ML(1+10′ at 121° C.)) determined according to the ASTM D 1646 method is 6 MU. The mechanical properties are shown in Table 1.

Example 11

Copolymer Monomer (a)/TFE 78/22 (Molar Ratio)

In a 5 lt autoclave, equipped with stirrer working at 630 rpm, there were introduced, after evacuation, 3.5 lt of demineralized water and 35 ml of microemulsion of perfluoropolyoxyalkylenes previously obtained as in example 1. The autoclave was then heated up to 60° C. and maintained at said temperature for the whole reaction. The following mixture of monomers was then fed: tetrafuoroethylene (TFE) 20% by moles, monomer (a) 80% by moles, so as to bring the pressure up to 0.5 MPa. In the autoclave there were then introduced: 3.5 gr of ammonium persulphate (APS) as initiator; 1.24 gr of 1,4-diiodoperfluorobutane (C₄F₈I₂) as polymer chain transfer agent; 0.5 gr of a bis-olefin of formula CH₂—CH—(CF₂)₆—CH═CH₂; the addition of the bis-olefin was carried out in 20 aliquots, each of 0.075 gr, starting from the beginning of the polymerization and for every 5% increase in the monomer conversion. The pressure of 0.5 MPa was maintained constant for the whole polymerization by feeding a mixture formed by: tetrafuoroethylene (TFE) 22% by moles, monomer (a) 78% by moles. After 240 minutes of reaction, corresponding to 100% of the monomer conversion, the autoclave was cooled and the latex discharged. The so obtained latex was coagulated as in example 9. 130 gr of polymer were obtained.

By ¹⁹F-NMR analysis of the polymer dissolved in hot C₆F₆ it was found that the molar percentage of monomer (a) in the polymer is 85%. The T_(g), determined by DSC, is −41,8° C. The Mooney viscosity (ML(1+10′ at 121° C.)) determined according to the ASTM D 1646 method is 5 MU.

Example 12

Terpolymer Monomer (a)/TFE/MVE 22/68/10 (Molar Ratio)

In a 5 lt autoclave, equipped with stirrer working at 630 rpm, there were introduced, after evacuation, 3.5 lt of demineralized water and 35 ml of microemulsion of perfluoropolyoxyalkylenes previously obtained as in example 1. The autoclave was then heated up to 70° C. and maintained at said temperature for the whole reaction. The following mixture of monomers was then fed: tetrafuoroethylene (TFE) 42% by moles, monomer (a) 31% by moles, methylvinylether (MVE) 27% by moles, so as to bring the pressure up to 0.9 MPa. In the autoclave there were then introduced: 0.75 gr of ammonium persulphate (APS) as initiator; 3.70 gr of 1,4-diiodo perfluorobutane (C₄F₈I₂) as polymer chain transfer agent; 1.8 gr of a bis-olefin of formula CH₂═CH—(CF₂)₆—CH═CH₂; the addition of the bis-olefin was carried out in 20 aliquots, each of 0.090 gr starting from the beginning of the polymerization and for every 5% increase in the monomer conversion. The pressure of 0.9 MPa was maintained constant for the whole polymerization by feeding a mixture formed by: tetrafuoroethylene (TFE) 59% by moles, monomer (a) 24% by moles, methylvinylether (MVE) 17% by moles. After 249 minutes of reaction, corresponding to 100% of the monomer conversion, the autoclave was cooled and the latex discharged.

The so obtained latex was coagulated as in example 9. 514 gr of polymer were obtained.

By ¹⁹F-NMR analysis of the polymer dissolved in hot C₆F₆, it was found that the molar percentage of monomer (a) is 22.6%, of TFE is 67.6%, of MVE is 9.8%. The T_(g), determined by DSC is −22.9° C. The Mooney viscosity (ML(1+10′ at 121° C.)) determined according to the ASTM D 1646 method is 29 MU. The mechanical properties are shown in Table 1.

Comments to Examples 9-12

The Applicant has unexpectedly found the versatility of monomer (a), shown in exs. 9-12, wherein the content of monomer (a) in the polymer ranges from 22% to 78% moles. As comparison, MOVE 1 does not allow to prepare polymers having such a wide range of compositions. TABLE 1 EXAMPLES 9 10 12 Formulation: Luperco 101 XL 45 phr 1.5 0.75 0.75 Drimix TAIC 75% ″ 2 1 1 ZnO ″ 5 5 5 Black MT N990 15 15 15 Mooney polymer ML_(121° (1+10)) 12 6 29 MDR 160° C., 12′ (ASTM D6204-97): ML Lbf. in. 0.26 0.03 0.44 MH ″ 17.03 5.42 17.72 ts2 ″ 26 52 53 t′50 ″ 35 58 75 t′90 ″ 67 122 180 Mechanical properties after post-cure at 230° C. for 1 + 4 h (ASTM D412-83) M100 Mpa 8.5 2.9 5.5 Stress at break ″ 11.6 5.1 9.9 Elong. at break % 123 151 130 Hardness Shore A 69 57 62 Compression set 200° C. for 70 h O-ring (ASTM D 395) % 26 29 29 TR 10 (ASTM D1329) ° C. −29 −36 −20 TR 70 (ASTM D1329) ° C. −44 −25 −10 

1. Perfluoroelastomers curable by peroxidic route having a glass transition temperature lower than −10° C., more preferably lower than −20° C., still more preferably lower than −35° C., in particular lower than −40° C., and a —COF end group amount in the polymer lower than the sensitivity limit of the following method: at the end of the polymerization, the polymer is isolated by coagulation by freezing and subsequent defrosting; it is washed twice with demineralizd water and is dried in a stove until a constant weight; the —COF end groups are determined by FT-IR spectroscopy, wherein on a polymer film having a thickness from 50 to 300 micron a scanning between 4,000 cm⁻¹ and 400 cm⁻¹ is initially carried out, the film being then kept for 12 hours in an environment saturated with ammonia vapours, and recording the IR spectrum under the same conditions of the initial IR spectrum; elaborating the two spectra by subtracting to the signals of the spectrum related to the untreated specimen (initial spectrum) the corresponding signals of the specimen spectrum after exposure to ammonia vapours, drawing the “difference” spectrum, normalized by the following equation: $\frac{``{{Difference}\quad{spectrum}}"}{\left\lbrack {{film}\quad{weight}\quad{(g)/{film}}\quad{area}\quad\left( {cm}^{2} \right)} \right\rbrack};$ the optical densities related to the —COF end groups, reacted with the ammonia vapours, are measured; the optical densities are converted into mmoles/kg of polymer by using the extinction coefficients reported in Table 1, page 73 of the report by M. Pianca et Al. “End groups in fluoropolymers”, J. Fluorine Chem. 95 (1999), 71-84 (herein incorporated by reference); obtaining the concentrations of the residual —COF end groups expressed as mmoles of end groups —COF/Kg of polymer: in the perfluoroelastomer spectrum no bands related to COF groups (1900-1830 cm⁻¹) are detectable, the method sensitivity limit being 0.05 mmoles/Kg.
 2. Perfluoroelastomers according to claim 1 comprising units deriving from bis-olefins of general formula:

wherein: R₁, R₂, R₃, R₄, R₅, R₆, equal to or different from each other, are H or C₁-C₅ alkyls; Z is a C₁-C₁₈ linear or branched alkylene or cycloalkylene radical, optionally containing oxygen atoms, preferably at least partially fluorinated, or a (per)fluoropolyoxyalkylene radical.
 3. Curable perfluoroelastomers according to claim 2, wherein the unit amount in the chain deriving from the bis-ole-fins of formula (I) is from 0.01 to 1.0% by moles, preferably from 0.03 to 0.5% by moles, still more preferably from 0.05 to 0.2 moles per 100 moles of the monomeric units, constituting the basic perfluoroelastomer structure, the monomer total sum being 100%.
 4. Curable perfluoroelastomers according to claim 2, wherein in formula (I) Z is preferably a C₄-C₁₂, more preferably C₄-C₈, perfluoroalkylene radical, while R₁, R₂, R₃, R₄, R₅, R₆ are preferably hydrogen; when Z is a (per)fluoropolyoxyalkylene radical, it comprises units selected from the following: —CF₂CF₂O—, —CF₂CF (CF₃)O—, —CFX₁O— wherein X₁=F, CF₃, —CF₂CF₂CF₂O—, —CF₂—CH₂CH₂O—, —C₃F₆O—.
 5. Curable perfluoroelastomers according to claim 2, wherein Z has formula: -(Q)_(p)—CF₂O—(CF₂CF₂O)_(m)(CF₂O)_(n)—CF₂-(Q)_(p)—  (II) wherein: Q is a C₁-C₁₀ alkylene or oxyalkylene radical; p is 0 or 1; m and n are numbers such that the m/n ratio is between 0.2 and 5 and the molecular weight of said (per)fluoropolyoxyalkylene radical is in the range 500-10,000, preferably 700-2,000.
 6. Curable perfluoroelastomers according to claim 5, wherein Q is selected from: —CH₂OCH₂—; —CH₂O(CH₂CH₂O)_(n)CH₂—, s being=1-3.
 7. Curable perfluoroelastomers according to claim 2, wherein the bis-olefin has formula: CH₂═CH—(CF₂)_(t0)—CH═CH₂ wherein t0 is an integer from 6 to
 10. 8. Curable perfluoroelastomers according to claim 2, wherein the bis-olefin has formula: CH₂═CH—(CF₂)₆—CH═CH₂  (b).
 9. Curable perfluoroelastomers according to claim 1 containing preferably iodine and/or bromine, more preferably iodine in amounts between 0.001% and 5% by weight, preferably between 0.01% and 2.5% by weight with respect to the total polymer weight.
 10. Curable perfluoroelastomers according to claim 9, wherein the iodine atoms are in the chain and/or in end position.
 11. Curable perfluoroelastomers according to claim 9, wherein alternatively or in combination with iodine, bromine is present, both in the chain and in end position.
 12. Curable perfluoroelastomers according to claim 1, comprising in admixture a semicrystalline (per)fluoropolymer, in an amount in percent by weight referred to the total of the dry weight of the mixture perfluoroelastomer+semicrystalline (per)fluoropolymer, from 0% to 70%, preferably from 0% to 50% by weight, still more preferably from 2% to 30% by weight.
 13. Curable perfluoroelastomers according to claim 12, wherein the semicrystalline (per)fluoropolymer is formed of tetrafluoroethylene (TFE) homopolymers, or TFE copolymers with one or more monomers containing at least one unsaturation of ethylene type, in an amount from 0.01% to 10% by moles, preferably from 0.05% to 7% by moles, said comonomers having an ethylene unsaturation both of hydrogenated and fluorinated type.
 14. Curable perfluoroelastomers according to claim 13, wherein the hydrogenated comonomers are selected from ethylene, propylene, acrylic monomers, styrene monomers.
 15. Curable perfluoroelastomers according to claim 13, wherein the fluorinated comonomers are selected from the following: C₃-C₈, perfluoroolefins; C₂-C₈ hydrogenated fluoroolefins; perfluoroalkylethylene CH₂═CH—R_(f), wherein R_(f) is a C₁-C₆ perfluoroalkyl; C₂-C₈ chloro- and/or bromo- and/or iodo-fluoroolefins; CF₂═CFOR_(f) (per)fluoroalkylvinylethers (PAVE), wherein Rf is a C₁-C₆ (per)fluoroalkyl; CF₂═CFOX (per)fluoro-oxyalkylvinylethers, wherein X is: a C₁-C₁₂ alkyl, or a C₁-C₁₂ oxyalkyl, or a C₁-C₁₂ (per)fluoro-oxyalkyl having one or more ether goups, for example perfluoro-2-propoxy-propyl; fluorodioxoles, preferably perfluorodioxoles.
 16. Curable perfluoroelastomers according to claim 12, wherein the comonomers are PAVEs and fluorodioxoles, preferably perfluorodioxoles.
 17. Compositions comprising: perfluoroelastomers according to claim 1, and perfluoroelastomers obtainable from polymers containing a —COF end group amount higher than 0.05 mmoles/Kg; the perfluoroelastomer amount according to claim 1 being at least 5-10% by weight, preferably 20-40% by weight, more preferably 50% by weight, with respect to the total weight of the perfluoroelastomers.
 18. Compositions according to claim 17, wherein the perfluoroelastomeric polymers containing —COF end groups in an amount higher than 0,05 mmoles/Kg comprise comonomers selected from the following: perfluorodioxoles, preferably having the following formula:

wherein Y═F, ORf₁, Rf₁ being a C₁-C₅ perfluoroalkyl, preferably Rf₁ is CF₃; X₁ and X₂, equal to or different from each other, are selected between F and CF₃, preferably F; Z₁ is selected between F, Cl, preferably F; perfluoroalkylvinylethers of formula CF₂═CFORf wherein Rf is a C₃ perfluoroalkyl; CF₂═CFOXa perfluorooxyalkylvinylethers, wherein Xa is C₃-C₁₂ perfluorooxyalkyl having one or more ether groups, for example perfluoro-2-propoxy-propyl; perfluorovinylethers (MOVE) of general formula CFX_(AI)═CX_(AI)OCF₂OR_(AI) (A-I) wherein R_(AI) is a C₂-C₆ linear, branched or C₅-C₆ cyclic perfluoroalkyl group, or a C₂-C₆ linear or branched when possible perfluorooxyalkyl group containing from one to three oxygen atoms; X_(AI)═F; the compounds of general formula: CFX_(AI)═CX_(AI)OCF₂OCF₂CF₂Y_(AI) (A-II) wherein Y_(AI)═F, OCF₃ are preferred; in particular (MOVE 1) CF₂═CFOCF₂OCF₂—CF₃ (A-III) and (MOVE 2) CF₂═CFOCF₂OCF₂CF₂OCF₃ (A-IV).
 19. Curable perfluoroelastomers according to claim 1 comprising the following monomers (percent by moles): A) from 1% to 100%, preferably from 5% to 100%, of the monomer of formula: CF₂═CFOCF₂OCF₃  (a) B) one or more perfluorinated comonomers having at least one unsaturation of ethylene type, from 0% to 99%, preferably from 0 to 95%; the sum of the monomer molar percentages being 100%; with the proviso that if the comonomer B) is TFE or the mixture of comonomers B) contains TFE, the TFE amount must be such that the polymer is elastomeric.
 20. Perfluoroelastomers according to claim 19, wherein when the copolymer does not contain other comonomers (B) besides TFE, the monomer amount of formula (a) is higher than about 15% by moles.
 21. Perfluoroelastomers according to claim 19, wherein comonomers B) are selected from the following: C₂-C₈ perfluoroolefins, preferably TFE, hexafluoropropene; perfluoroalkylvinylethers of formula CF₂═CFORf wherein Rf is a C₁-C₂ perfluoroalkyl, preferably Rf═—CF₃.
 22. Perfluoroelastomers according to claim 21, wherein the comonomer B) is tetrafluoroethylene (TFE) and/or perfluoromethylvinylether (MVE).
 23. Perfluoroelastomers according to claim 19, having the following monomer compositions, expressed in % by moles, the sum of the monomer molar percentages being 100%: monomer of formula (a): 100%; preferably monomer of formula (a): 99.0%-99.99% bis-olefin of formula (b) 1%-0.01%; still more preferably monomer of formula (a): 99.90-99.99%, bis-olefin of formula (b) 0.1-0.01%; monomer of formula (a): 15-40%, TFE: 60-85%; preferably monomer of formula (a): 18-30%, TFE: 69-81.99%, bis-olefin of formula (b) 1-0.01%; monomer of formula (a): 40-99%, TFE: 1-60%; preferably monomer of formula (a): 39-98.99%, TFE 1-60%, bis-olefin of formula (b) 1-0.01%; monomer of formula (a): 5-40%, MVE: 5-30%, TFE: 50-85%; preferably monomer of formula (a): 5-40%, MVE: 5-30%, TFE: 50-85%, bis-olefin of formula (b) 1-0.01%; monomer of formula (a): 40-99%, MVE: 5-30%, TFE: 1-60%; preferably monomer of formula (a): 40-99%, MVE: 5-30%, TFE: 1-60%, bis-olefin of formula (b) 1-0.01%.
 24. Cured perfluoroelastomers according to claim
 1. 25. Manufactured articles obtainable with the perfluoroelastomers of claim
 24. 26. A process to obtain the monomer CF₃OCF₂OCF═CF₂ comprising the following steps: I obtainment of the fluoroformate CF₃OCOF; II reaction of the fluoroformate CF₃OCOF with elemental fluorine and olefinic compounds having formula: CAF═CA′F  (IV) and obtainment of the fluorohalogenether of formula CF₃OCF₂OCFACF₂A′  (V) wherein A and A′, equal to or different the one from the other, are H, Cl or Br, with the proviso that both are not H; the temperature being between −120° C. and −20° C.; III obtainment from the fluorohalogenether of formula (V) of the monomer of formula (a) by a reaction wherein the substituents A and A′ are removed from the fluorohalogenether; wherein in step I the fluoroformate CF₃OCOF is prepared by reaction of CF₃OF and CO at temperatures between 80° C. and 250° C., preferably between 120° C. and 230° C., still more preferably between 150° C. and 200° C.
 27. A process according to claim 26, wherein in step I the molar ratio CF₃OF/CO is between 0.1 and 10, preferably between 0.2 and 5, more preferably between 0.5 and
 2. 28. A process according to claim 26, wherein the reaction mixture containing CF₃OCOF obtained in step I is directly fed, without separation of the mixture components, in the reactor of step II.
 29. A process according to claim 26, wherein the material of which the reactor wherein step I takes place is constituted, is selected from glass, inert perfluorinated plastics, preferably PTFE, PFA; or metal alloys coated inside with glass or with perfluorinated plastics.
 30. Use of the perfluoroelastomers according to claim 1 to obtain manufactured articles usable from temperatures lower than −10° C. up to 300° C., having improved mechanical and elastomeric properties. 